Plating with Zinc-Nickel: Benefits and Challenges (2024)

Q. Can you explain the benefits of zinc-nickel and provide an overview of alkaline versus acid zinc-nickel?

A. Zinc-nickel has increasingly become the finish of choice for many industries with high-corrosion and high-performance needs. It is a rapidly growing segment of the electroplating market, nearly quadrupling in usage in the last five years. The alloy has many properties that are appealing to manufacturerswithin the fastener, casting, automotive and heavy equipment industries. It is also gaining usage in the defense industry as a potential replacement for cadmium. Zinc-nickel offers superior corrosion resistance, with most deposits at a 12-to-15% alloy range producing a coating that can achieve 250+ hours to first white corrosion and 1,000+ hours to first red corrosion.

Hardness, heat resistance and high-alloy benefits

Zinc-nickel has a Vickers hardness of 400 to 500 HV — zinc-only deposits only have a hardness of around100 HV. Because handling and assembly can be a destructive process for softer coatings like zinc and zinc flake, zinc-nickel’s combination of hardness and overall corrosion protection make thealloy deposit ideal for fasteners or components that require further handling or assembly.

Another excellent benefit of the zinc-nickel alloy deposit is its overall resistance to heat. Many industry specs require baking, and the zinc-nickel deposit can withstand baking temperatures in excess of 200°C for fourhours while still achieving800 hours of neutral salt spray protection to first red rust. Zinc-nickel is commonly used on stampings and fasteners for barrel applications, and heavily used on brake component castings in rack applications.

Most availablezinc-nickel systems produce a similar alloy deposit, with an average alloy range of 12-to-15% nickel content. Early systemsincluded a lower alloy of 5-to-7%, butthose systems are obsolete.The chemical technology available in today’s higher-alloy systems produces a bright and ductile deposit with an even thickness and alloyed distribution over a wide current density range. Zinc-nickel is also the best coating choice when a black appearance is needed in the finished part, as the nickel in the alloy suits blackening.

Alkaline vs. acid zinc-nickel

Between alkaline zinc-nickel and acid zinc-nickel, alkaline zinc-nickel has a much larger market share— thoughacid zinc-nickel is rapidly gaining ground. Two main benefits of the alkaline zinc-nickel process are even distribution and ductility. Alkaline zinc-nickel offers a more even distribution across the current density ranges, making it ideal for plating complex geometries. The superior ductility of the deposithelps minimize cracking to maintainproper corrosion protection. As a result, manufacturers can subject alkaline zinc-nickel depositsto bending or crimping operations after plating. This is one of the primary reasons the automotive industry heavily usesalkaline zinc-nickelfor brake lines.

One majorbenefit of acid zinc-nickel is thatit provides superior activation compared to alkaline. This makes acid zinc-nickel a highly preferred method for plating over castings and other high-carbon, heat-treated steel components like calipers. In addition, acid zinc-nickel offers faster plating speeds due to its high efficiency, and acid zinc-nickel systems’generalease-of-useat a wide array of current densitiesprovides plating shops increased flexibility. Platers can run an array of current densities and still get a good part.

New solutions for acid-zinc nickel difficulties

There are several important operational considerations to keep in mind when running an acid zinc-nickel process. When not in use, anodes must be removed and cleaned prior to reuse. Older technology systems also requiredual anodes and dual rectifiers, resulting in added cost and maintenance. Newer systems can operate on a single rectifier with specific adjustments to the anode ratio.

Another important operational factor to consider when evaluating an acid zinc-nickel process is the amount of total chlorides in the system. In the past, platersfrequently experienced issues withammonium chloride and high salt content in the process, which resulted in harder-to-control parameters and requiredconstant elevated temperatures to stop the baths from salting out. The higher-salt solutions could clog air lines, filters, anodes, heat exchangers and cooling lines,meaning the bath would often need costly maintenance downtime in the form of decantingor pumpingout and cleaningto remove the precipitate.

Fortunately, newer acid zinc-nickel systems can operate at lower, more economical temperatures compared to the high-salt systems. These newer processes are lower in total chlorides and offer a large operating window in the temperature range to eliminatethe common problem of the bath salting out if it cools down. The lower operating temperatures also reduce unnecessary energy costs. Check with your chemistry supplier to ensure the process you are evaluating utilizes the newer technology with lower chlorides to avoid the issues mentioned above.

Looking to the future

Due to its high corrosion protection and heat tolerance, zinc-nickel offers many benefits and meets the demanding specifications of automotive, heavy equipment and similar OEMs. These industries will continue to serve ascatalysts for growth and opportunity.

An important factor for success when plating alkaline or acid zinc-nickel alloys is working with a chemistry supplier who deeply understands the characteristics of alloy components and the different “levers” the supplier can pullto dial in the chemistry toyour specific plating needs.